DINITROL 4010 CORROHEAT
Code: DA3670
Resistant corrosion inhibitor for surface and engine protection
500ml aerosol
Resistant corrosion inhibitor for surface and engine protection.
DINITROL 4010 Corroheat is versatile and can be used in both open and closed areas. The product penetrates like a cavity wax. It can also be used in electrical systems to avoid galvanic corrosion and other negative influences such as moisture.
> High mechanical resistance
> High temperature resistance
> Excellent adhesion
Long-term protection
Product Description
DINITROL 4010 Corroheat leaves a hard, transparent film that is resistant to both alkali and acids and is heat resistant up to a temperature of 200°C. It has a tack-free and clean film which facilitates a visual inspection of metal surfaces, reading of labels and numbers etc.
Applications
The adhesion and flexibility on rubber and plastic parts at both low and high temperatures are very good. Appropriate parts to be treated with DINITROL 4010 Corroheat are engine compartments, engines and other parts which have to withstand high temperatures.
Method of Use
DINITROL 4010 Corroheat should be applied on a clean, dry surface. High or low pressure equipment can be used, airless or airmix. Application temperature between 15 – 30°C. Product hardness, flexibility and adhesion increases at higher drying temperatures.
Pre-treatment Substrates
Surfaces shall be dry, clean and free from corrosion.
Over-Coating
Normally not to be overpainted.
Details
> Colour - Transparent beige
> Type of film - Hard, waxy
> Density at 23°C 890 kg/m³
> Viscosity at 23°C, DIN 4 25 seconds
> Dry matter content 47% by weight
> Aromatic part in the solvent 0,5 %
> Recommended film thickness wet 120 μm
> Recommended film thickness 40 μm
> Drying time 120 µm wet, 1 h with optimal ventilation 120 µm wet, 4-6 hours at RT 23°C 50% RH
> Low temperature adhesiont -30°C
> Effect on car paint - none
> Removability within 3 months
> Hydrocarbon solvents
> Heat resistance Short-term 200°C / Long-term 160°C
> Salt spray test (drying 24 h, 80°C) 240 hrs 40 microns dry 500 hrs 80 mircrons dry